Plasticized PVC Compounds for General Purpose Electrical Applications |
|
Specific Gravity |
Tensile Strength |
Elongation at Break |
Shore (A) Hardness (15") |
Cold flex Temperature |
Volume Resistivity |
Exercise Temperature |
V.D.E. 0207/86 |
Type |
Applications |
Test Method U.M. |
ISO 1183
Kg / dm3 |
ISO R/527 N/mm2 |
ISO 527
% |
ISO 868 |
ISO 458/2 C |
ASTM D 257
Ohm.cm |
ISO R/182/A
min. |
|
RC/86/3/Z |
Primary & secondary insulation sheeting |
1.49 |
17 |
300 |
86 |
-15 |
6 x 10¹³ |
60 |
|
RC/76/1/Z |
Primary & secondary insulation sheeting |
1.44 |
13 |
300 |
76 |
-30 |
2 x 10¹³ |
78 |
|
|
|
Specific Gravity |
Tensile Strength |
Elongation at Break |
Shore (A) Hardness (15") |
Cold flex Temperature |
Volume Resistivity |
Exercise Temperature |
V.D.E. 0207/86 |
Type |
Applications |
|
Test Method U.M. |
ASTM D 792 g/cm |
ASTM D 638 kg/cm |
ASTM D 638 % |
ASTM D 2240 |
ASTM D 1043 C |
20 C |
RC/92 |
Primary insulation |
1.38 |
230 |
320 |
94 |
-15 |
6x10 |
80 |
YM 5 |
RC/94/T |
High speed insulation for telephone cable |
1.31 |
220 |
300 |
94 |
-18 |
1x10 |
70 |
|
|
|
|
|
|
|
|
|
|
|
RC/75 |
Sheeting |
1.38 |
230 |
320 |
94 |
-15 |
6x10 |
80 |
YM 5 |
RC/78 |
Primary & secondary insulation / sheeting for glossy cable |
1.26 |
180 |
370 |
78 |
-30 |
5x10 |
70 |
YM 2 |
RC/83 |
Primary & secondary insulation / sheeting for glossy cable |
1.34 |
180 |
320 |
83 |
-30 |
6x10 |
70 |
YM 1 |
RC/75/K |
Coaxial sheeting / further applications in building industry |
1.34 |
180 |
320 |
83 |
-30 |
6x10 |
70 |
|
RC/82/K |
Coaxial cable |
1.35 |
180 |
360 |
82 |
-30 |
5x10 |
70 |
|
RC/80/C |
Transparent cable |
1.25 |
180 |
320 |
80 |
-30 |
|
70 |
YI 1 |
Technical information contained is based on Rokyplast general experience and is given in good faith but Rokyplast is not responsible for factors or events outside its knowledge or control. |